Engineered metals
for precision industries

www.robertlaminage.com

MSDS (pdf) Quote request

ROBERT 15
C75S

Chemical composition

Ni0.4 max

P0.025 max

FeBAL

Mn0.60-0.90

Si0.15-0.35

S0.025 max

C0.70-0.80

Mo0.10 max

Cr0.40 max

*Unified Numbering System (USA)

Low-alloy steel used for deep-drawing parts which can then be hardened by quenching.

Physical properties		Units
Density (20°C)	7,85	Kg/dm³
Melting point	1400-1500	°C
Longitudinal elasticity modulus	210	GPa
Thermal conductivity		W/m·K
Electrical conductivity	7,7	m/Ω·mm²
Electrical resistivity	0,13	µΩ·m
Linear expansion Coefficient	12	10⁻⁶·K⁻¹
IACS (International Annealed Copper Standard)	13	%
Poisson's ratio

1 poor | 2 average | 3 good | 4 very good | - no info

Heat Treatment / Hardening
Annealing temperature	650-720	°C
Temperature for stress relief treatment		°C
Hardening temperature	790-820	°C
Hardening treatment time		hour(s)

Hardening by quenching (rapid cooling) followed by tempering to reduce metal brittleness

ROBERT 15
Possible hardness range	145 - 880	HV
Possible Rm range	500 - 2800	MPa

Grade	According to standard	Hardness (HV: Vickers) min - max	Rm (MPa) min - max	Rp 0.2 (MPa) min - max	Elongation (%) where L0 = 100mm min - max	L0	Grain size (µm) min - max

Do not hesitate to ask us for your specific grades and parameters. We can make productions according to your needs.