Alloy name Physical properties Capabilities Mechanical property
RLSA
alloy name
Groups Designation Standard chemical comp.
(percentage by weight)
RLSA no. EN standard DIN standard UNS no. Density
20° C
Melting
point
Longitudinal
elasticity modulus
Thermal
conductivity
Electrical
conductivity
Electrical
resistivity
Linear expansion
coefficient from 20 to 300° C
IACS (International
Annealed Copper Standard)
Poisson's
ratio
Corrosion
resistance
Cold
deformation
Hot
deformation
Electro-
depositing
Diamond cutting / Planing
/ Etching
Nitriding Mechanical
polishing
Electrolytic
polishing
Hot
tinning
Tin
soldering
Brazing Welding
without filler
TIG Resistance
welding
Machining Hardness
range
Rm range Al range
AISI 316L 1.4404 Aciers Inoxydables INOX Fe reste Cr16.5-18.5 Ni10-13 Mo2-2.5 C0-0.03 964 1.4404 7,98 1375-1400 15 0,75 16.5-19.5 0.27-0.28 165 - 430 - - 48
AISI 316L 1.4435 Aciers Inoxydables INOX Fe reste Cr17-19 Ni12.5-15 Mo2.5-3 C0-0.03 966 1.4435 7,98 1370-1400 15 0,75 16.5-19.5 0,3 195 - 430 - -
Al 1050 (99.5) Aluminium ALUMINIUM Al99.5 800 AW-1050A 3.0255 A91050 2,71 640-660 69 210-230 >34 <0.029 23,6 59 0,33 4 4 4 1 4 4 1 30 - 45 - -
Al 1080 (99.8) Aluminium ALUMINIUM Al99.8 808 AW-Al99.8 3.0285 2,70 640-660 225 0,03 62 0,33 4 18 - 35 60 - 150 -
Al 1350 (Spécial 99.5) Aluminium ALUMINIUM Al99.5 Spécial (peu d'impureté) 805 AW-1350A 3.0257 A91350 2,71 640-660 4 20-45 65-160 2 - 40
AlCuMgSi Aluminium AVIONAL 102 - EN AW2017A Al reste Cu3.5-4.5 Mg0.4-1 Si0.2-0.8 Mn0.4-1 870 AW-2017A 3.1325 2,78 510-650 72 135 >27 <0.037 23,6 47 0,33 1 4 4 2 2 2 3 55 - 180 240 - 330 -
AlMg3 Aluminium PERALUMAN 300 Al reste Mg2.6-3.6 830 AW-5754 3.3535 A95754 2,67 600-645 70 130-140 >19 <0.053 23,8 33 0,33 4 4 4 2 4 3 1 70 - 100 230 - 320 -
AlMgSi1 Aluminium ANTICORODAL 110 Al reste Mg0.6-1.2 Si0.7-1.3 Mn0.4-1 860 AW-6082 3.2315 A96082 2,71 580-650 69 200-220 >31 0,032 23,5 53 3 4 3 3 3 3 2 40 - 150 120 - 320 -
AlMn1 Aluminium ALUMAN 100 Al reste Mn0.9-1.5 810 AW-3103 3.0515 2,73 640-660 69 160-190 >24 0,042 23,2 41 0,33 4 4 4 1 4 4 1 25 - 50 95 - -
AlZn5.5MgCu Aluminium PERUNAL Al reste Zn5.1-6.1 Mg2.1-2.9 Cu1.2-2 855 AW-7075 3.4365 2,81 475-635 115-140 17-20 0,052 23,5 33 2 2 2 1 3 4 - - -
AM388 Bronzes durcissables (Spinodal) CuNi8Sn5 Cu reste Ni7-8 Sn4.5-5.5 555 C72650 8,87 1120 127 29 >4.7 <0.215 16,4 8 4 4 1 3 4 4 3 3 3 3 4 4 3 4 130 - 335 570 - 1010 -
ARCAP AP1 ARCAP Cu65Ni25Zn9 Cu63-67 Ni24-26 Zn reste 464 8,75 1130 163-170 22 >25 <0.40 17 >4.30 4 4 1 4 3 4 4 4 2 1 4 3 120 - 220 370 - 680 0 - 40
ARCAP AP1 C ARCAP Cu56Ni25Zn18 Cu55-57 Ni24-26 Zn reste 465 8,80 1170 163-170 22 >25 <0.40 17 >4.30 4 4 1 4 3 4 4 4 2 1 4 3 110 - 220 450 - 750 -
ARCAP AP4 ARCAP CuNi44Mn Cu reste Ni43-45 Mn0.5-2 466 2.0842 8,90 1290 145 22 >25 <0.49 17 >3.5 4 4 3 4 3 4 4 4 2 1 4 3 100 - 235 460 - 750 - 52
B98 Alliages à haute conductibilité CuNi1P Cu reste Ni0.9-1.2 P0.15-0.25 Pb0.02 max 198 CW108C C19000 8,90 1038-1082 127 253 >29* <0.0345* 18 >50* 0,34 4 4 3 4 2 85 - 210 300 - 700 -
Cu ETP Cuivre CUIVRE - CuA1 Cu>99.9 O0.04 max 100 CW004A 2.0065 C11000 8,94 1083 127 390 >55 <0.0188 17,7 >95 4 4 3 4 3 4 3 4 3 3 4 1 60 - 130 225 - 380 1 - 38
Cu OF Cuivre CUIVRE - CuC1 Cu>99.99 O0.001 max 125 CW008A 2.0040 C10200 8,94 1083 127 390 58 <0.017241 17 100 4 4 3 4 3 4 3 4 3 3 4 1 57 - 125 225 - 360 - 38
Cu OFE Cuivre CUIVRE - CuC2 Cu>99.99 O0.0005max 120 CW009A C10100 8,94 1083 127 390 58 <0.017241 17 100 4 4 3 4 3 4 3 4 3 3 4 1 75 - 125 225 - 360 -
CuNi12Zn24 Maillechort MAILLECHORT Cu63-66 Ni11-13 Zn reste Pb0.03 max 400 CW403J 2.0730 C75700 8,67 1020-1065 125 42 >3 <0.333 18 >5 0,32 4 4 1 4 4 4 4 2 2 2 3 2 80 - 230 395 - 700 - 45
CuNi12Zn25Pb Maillechort au plomb MAILLECHORT Pb Cu60-63 Ni11-13 Zn reste Pb0.5-1.5 490 CW404J C79200 8,67 1020 130 33 >4.35 <0.23 16 >7.5 0,34 4 3 1 3 2 1 1 2 1 1 2 4 100 - 230 480 - 800 -
CuNi15 Cupronickel CUPRONICKEL Cu reste Ni14-16 615 8,90 1130 75 16 - - -
CuNi18Zn20 Maillechort MAILLECHORT Cu60-63 Ni17-19 Zn reste Pb0.03 max 420 CW409J 2.0740 C76400 8,72 1055-1105 135 33 >2 <0.50 17,7 >3 0,34 4 4 1 4 4 4 4 3 2 2 3 3 80 - 250 410 - 715 - 40
CuNi18Zn27 Maillechort MAILLECHORT Cu53-56 Ni17-19 Zn reste Pb0.03 max 455 CW410J 2.0742 C77000 8,70 1040-1090 140 32 >2 <0.5 17,7 6 0,34 4 4 1 4 4 4 4 3 2 2 3 3 80 - 250 410 - 715 -
CuNi25 Cupronickel CUPRONICKEL Cu reste Ni24-26 625 2.0830 8,90 1150-1220 33 0,34 16,3 5 - - -
CuSn3Zn9 Bronze Chrysocale CHRYSOCALE Cu reste Sn1.5-3 Zn7.5-10 Pb0.03 max 520 CW454K C42500 8,75 1010-1030 112 120 >11.76 <0.085 18,3 28 0,34 2 4 1 4 4 4 3 3 4 4 3 3 2 2 80 - 225 300 - 660 -
CuSn6 Bronze BRONZE Cu reste Sn5.5-7 Pb0.03 max 506 CW452K 2.1020 C51900 8,80 900-1050 118 75 >8 <0.125 18,5 >13 2 4 1 4 4 3 3 4 4 2 3 3 3 2 124 - 240 370 - 820 3 - 45
CuSn8 Bronze BRONZE Cu reste Sn7.5-8.5 Pb0.03 max 508 CW453K 2.1030 C52100 8,80 900-1050 115 63 >7.5 <0.133 18,2 >13 3 4 1 4 4 3 3 4 4 2 3 3 3 2 90 - 240 380 - 720 1 - 45
CuZn10 Tombac TOMBAC Cu89-91 Zn reste 210 CW501L 2.0230 C22000 8,80 1040-1050 124 184 >21.46 <0.0466 18,2 >37 4 3 2 4 4 4 4 4 4 3 3 3 1 50 - 175 250 - 540 0 -
CuZn15 Tombac TOMBAC Cu84-86 Zn reste 250 CW502L 2.0240 C23000 8,75 1020-1030 122 159 >17.40 <0.0575 18,5 >30 4 3 2 4 4 4 4 4 4 3 3 3 1 65 - 180 280 - 550 -
CuZn28 Laiton LAITON Cu71-73 Zn reste Pb0.03 max 300 CW504L 2.0261 C25600 8,55 915-965 114 130 >16.5 <0.06 19,7 >29 3 4 3 4 4 4 4 4 4 4 3 2 3 1 55 - 210 270 - 580 - 50
CuZn30 Laiton LAITON Cu69-71 Zn reste Pb0.03 max 330 CW505L 2.0265 C26000 8,55 945-965 114 126 >12.76 <0.0784 19,7 >28 3 4 3 3 3 4 4 4 4 4 3 2 3 1 55 - 200 270 - 630 -
CuZn33 Laiton LAITON Cu66-68 Zn reste Pb0.03 max 333 CW506L 2.0280 C26800 8,50 900-920 112 120 >11.60 <0.0862 19,9 >20 3 4 3 3 3 4 4 4 4 4 3 2 3 1 55 - 210 280 - 650 -
CuZn37 Laiton LAITON Cu62-64 Zn reste Pb0.03 max 370 CW508L 2.0321 C27200 8,44 900-920 110 120 >11.60 <0.0862 20,2 >28 3 4 3 2 2 4 2 4 4 4 3 2 3 2 55 - 220 300 - 700 -
CuZn37Pb2 Laiton au plomb LAITON Pb Cu61-63 Zn reste Pb1.6-2.5 385 CW606N (C35300) 8,45 885-910 110 105 14,7 0,068 20,4 25 3 2 1 1 2 3 2 4 4 2 1 1 2 4 75 - 200 360 - 700 -
CuZn38Pb2 Laiton au plomb LAITON Pb Cu60-63 Zn reste Pb1.6-2.5 390 CW608N 2.0371 C35000 8,44 885-910 102 109 13,9 0,07 20,4 24 3 2 1 1 2 3 2 4 4 2 1 1 2 4 75 - 210 360 - 700 1 - 28
CuZn39Pb2 Laiton au plomb LAITON Pb Cu58-61 Zn reste Pb1.6-2.5 397 CW612N 2.0380 C37700 8,44 885-910 102 109 13,9 0,07 21,1 24 3 2 1 1 2 3 2 4 4 2 1 1 2 4 80 - 200 360 - 700 -
CuZn42 Laiton LAITON Cu57-59 Zn reste Fe0-0.35 Pb0.03 max 342 CW510L C28500 8,40 900 105 139 20,2 31 3 4 3 2 2 2 4 4 70 - 220 - -
CuZn42 (PNA378) Laiton LAITON Cu57-58.5 Zn reste Fe0.1-0.5 Pb0.03 max 343 CW510L C28500 8,40 900 105 139 20,2 31 3 4 3 2 2 2 4 4 90 - 220 - -
CuZn42 (PNA380) Laiton LAITON Cu57-58.5 Zn reste Fe0-0.01 Pb0.03 max 344 CW510L C28500 8,40 900 105 139 20,2 31 3 4 3 2 2 2 4 4 70 - 220 - -
CuZn5 Tombac TOMBAC Cu94-96 Zn reste 200 CW500L 2.0220 C21000 8,86 1050-1065 127 234 32,3 0,031 17 56 4 3 2 4 4 4 4 4 4 3 3 3 1 45 - 135 250 - 420 -
DECLAFOR 1015 Bronzes durcissables (Spinodal) CuNi7.5Sn5 Cu reste Ni7-8 Sn4.5-5.5 Mn0.05-0.3 565 8,80 960 115 53,6 >5.22* <0.1916* 17,25 13* 4 3 1 4 4 4 3 3 4 3 4 4 3 4 120 - 325 455 - 940 - 30
Hastelloy C-276 Alliage Nickel NiMo16Cr15W Ni51-63Mo15-17Cr15-16.5Fe4-7W3-4.5 986 NiMo16Cr15W 2.4819 N10276 8.89 1325-1370 208-143 (20-1000°C) 10.2-27.2 (20-1000°C) 4 sauf acide nitrique 3 3 250 Min 730 Min 30% Max
K55 Alliages Spéciaux CuNi3Si1Mg Cu reste Ni2.2-4.2 Si0.25-1.2 Mg 0.05-0.3 145 CW112C C70250 8,82 1040-1060 190 17,6 43 0,34 - - -
K65 Alliages Spéciaux CuFe2P Cu reste Fe2.1-2.6 P0.03 max 130 CW107C 2.1310 C19400 8,90 1100 123 280 >35 <0.02857 17,6 64 0,34 4 3 3 4 1 90 - 175 330 - 520 -
L49 Alliages Spéciaux CuNi9Sn2 Cu reste Ni8.5-10.5 Sn1.8-2.8 Pb0.03 max 540 CW351H 2.0875 C72500 8,89 1060-1130 140 48 >4.64 <0.2155 17,6 11 0,34 2 4 3 4 4 3 3 4 4 3 3 3 4 1 75 - 200 340 - 600 - 40
MONEL 400 Cupronickel NiCu32Fe1.5Mn Ni63 min Cu28-34 Fe1-2.5 Mn0-2 430 2.4360 N04400 8,83 1300-1350 179 22 3,6 55 13,9 4 oui oui 150 - 550 - - 40
Ni 99.0 Nickel Ni 99.0 Ni99.0 C0-0.15 601 2.4068 8,89 1435-1446 88 70-240 - -
Ni 99.2 Nickel Ni 99.2 Ni99.2 C0-0.1 602 2.4066 8,89 1435-1446 88 70-240 - -
Ni 99.6 Nickel Ni 99.6 Ni99.6 C0-0.08 600 2.4060 8,89 1435-1446 88 70-240 - -
Ni 99.6 (low carbon) Nickel LC-99.6 LC-99.6 C0-0.02 606 2.4061 8,89 1435-1446 88 21 70 - 240 - -
NICLAFOR 1000 Bronzes durcissables (Spinodal) CuNi9Sn6 Cu reste Ni8.5-9.5 Sn5.5-6.5 560 C72700 8,90 968-1078 120 53,6 >5.22* <0.1916* 17,25 9* 4 4 1 4 4 4 4 3 90 - 360 410 - 1100 1 - 40
NKT322 Cuivre Titane CuFeTi Cu reste Fe0.17-0.23 Ti2.9-3.4 135 C19910 8,70 965-1055 66,8 0.132-0.172 18 10-13 300 - 360 950 - 1200 18 - 3
PFINODAL Bronzes durcissables (Spinodal) CuNi15Sn8 Cu reste Ni14.5-15.5 Sn7.5-8.5 550 C72900 8,94 950-1115 127 29 >4.7 <0.215 16,4 8 4 4 1 3 4 4 3 3 3 3 4 4 3 4 140 - 400 570 - 1250 0 - 39
PHYNOX - ELGILOY Aciers Inoxydables spécial CoCr20Ni16Mo7 Fe reste Co39-42 Cr18.5-21.5 Ni15-18 Mo6.5-7.5 Mn1-2.5 C0-0.15 974 R30003/R30008 8,30 1450-1460 12,5 1,1 0,95 12,5 0,34 230 - 670 900 - 2600 -
POLIDUR Aciers Maraging (Nickel Cobalt) X2 NiCoMo18-16.5-5 Fe reste Ni17-19 Co16-17 Mo4.5-5.5 971 8,14 1430-1460 9,5 0,3 2 2 3 4 3 3 3 310 - 500 700 - 1950 -
RAFFINAL Aluminium Al 99.99% Al99.99 801 AW-Al99.99 A91199 2,70 660 72 243 0,027 64 0,33 4 16 - 30 35 - 100 2 - 45
ROBAMAG Aciers Inoxydables spécial INOX - 13Rm19 Fe reste Cr17.5-19.5 Ni6.8-8.5 Mn5-7.5 N0.2-0.3 C0.07-0.15 976 1.4369 7,90 1400-1450 15 0,7 18 0,28 235 - 850 - 1600 2 - 45
ROBERT 02 Fer Pur Fer PUR - RFe60 Fe reste C0-0.03 901 1.1015 7,86 1400-1500 210 45-55 7,7 0,6 12 12 1 4 4 3 100 - 200 240 - 610 3 - 50
ROBERT 12 Aciers faiblement alliés C60S Fe reste C0.57-0.65 Mn0.6-0.9 Si0.15-0.35 912 C60S 1.1221 7,85 1400-1500 210 45-55 7,7 0,13 12 13 0,29 1 4 4 4 3 150 - 840 460 - 2700 - 30
ROBERT 12 (dev. Mn) Aciers faiblement alliés C60S (dev. Mn) Fe reste C0.57-0.65 Mn0.3-0.5 Si0.15-0.35 916 C60S (dev. Mn) 1.1221 (dev. Mn) 7,85 1400-1500 210 45-55 7,7 0,13 12 13 0,29 1 4 4 4 3 120 - 840 410 - 2700 -
ROBERT 14 Aciers faiblement alliés C67S Fe reste C0.65-0.73 Mn0.6-0.9 Si0.15-0.35 914 C67S 1.1231 7,85 1400-1500 210 45-55 7,7 0,13 12 13 0.27-0.30 1 3 4 4 3 120 - 840 470 - 2700 -
ROBERT 15 Aciers faiblement alliés C75S Fe reste C0.7-0.8 Mn0.6-0.9 Si0.15-0.35 915 C75S 1.1248 7,85 1400-1500 210 45-55 7,7 0,13 12 13 1 3 4 4 3 145 - 880 500 - 2800 -
ROBERT 2 Fer StW24 Fe reste C0-0.08 Mn0-0.4 902 DC04 1.0338 7,85 1400-1500 210 45-55 7,7 0,13 12 13 0,3 1 4 4 3 100 - 200 300 - 610 - 44
ROBERT 20 Aciers faiblement alliés C100S Fe reste C0.95-1.05 Mn0.3-0.6 Si0.15-0.35 920 C100S 1.1274 7,85 1400-1500 210 45-55 7,7 0,13 12 13 0,29 1 3 4 4 3 150 - 900 440 - 2900 -
ROBERT 3 Fer alliés 9SMnPb28 Fe reste C0-0.14 S0.27-0.33 Mn0.9-1.3 Pb0.15-0.35 903 1.0718 7,85 1500-1540 1 4 4 100 - 200 300 - 610 -
ROBERT 30 Aciers Inoxydables INOX Fe reste Cr16-19 Ni6-9.5 C0.05-0.15 960 1.4310 S30100 7,90 1400-1425 0,29 3 170 - 560 520 - 2000 -
ROBERT 31 Aciers Inoxydables INOX Fe reste Cr17-19.5 Ni8-10.5 C0-0.07 961 1.4301 S30400 7,90 1400-1460 15 0,73 16-18.5 0,29 3 180 - 480 550 - 1600 -
ROBERT 32 Aciers Inoxydables INOX Fe reste Cr16-19 Ni6-9.5 C0.05-0.15 962 1.4310 (+C) S30100 7,90 1400-1425 0,29 3 215 - 570 700 - 1950 1 - 20
ROBERT 7 Aciers alliés 42CrMo4 Fe reste C0.32-0.42 Cr0.9-1.2 Mo0.15-0.3 907 1.7225 7,85 1420-1460 0,29 130 - 260 360 - 860 3 - 30
RODUR Aciers Maraging (Nickel Cobalt) X2 NiCoMo18-9-5+Ti Fe reste Ni17-19 Co8-10 Mo4.5-5.5 Ti0.5 C0-0.03 970 1.6358 K93120 8,10 1430-1460 185-195 19,7 0,44 9,5 0,3 2 4 3 3 3 3 3 310 - 600 1000 - 2100 - 5
RODUR Std Aciers Maraging (Nickel Cobalt) X2 NiCoMo18-9-5+Ti Fe reste Ni17-19 Co8-10 Mo4.5-5.5 Ti0.5-0.8 C0-0.03 977 1.6358 K93120 8,10 1430-1460 185-195 19,7 0,44 9,5 0,3 2 4 3 3 3 3 3 310 - 600 1000 - 2100 - 5
S23 Alliages Spéciaux CuZn23Al3Co Cu72-75 Zn reste Al3-3.8 Co0.25-0.55 Pb0.03 max 375 CW703R C68800 8,23 950 116 78 >9 <0.11 18,2 17 0,34 3 4 3 4 3 1 1 2 1 2 3 2 155 - 250 510 - 900 -
SANDVIK 316LVM Aciers inoxydables X 2 CrNiMo 18 15 3 Fe Reste Cr17.5 Ni14 Mo2.8 Mn1.7 967 1.4441 S31673 8.0 g/cm3 200 MPa 14W /(m °C) 16.5 per °C 800-1300 116-189
Siclanic S Alliages à haute conductibilité CuNiSi Cu reste Ni1.8-3.0 Si0.4-0.8 150 CW111C 2.0855 C18000 8,84 1040-1060 225 35 17,5 48 80 - 150 - -
STOL 80 Cuivre CuSn0.15 Cu reste Sn0.1-0.2 161 CW117C** C14415 8,93 1083 130 364 >49 <0.024 18 >85 0,34 4 4 3 4 3 3 3 3 4 3 3 3 2 65 - 125 250 - 450 -
TITANE Gr. 1 Titane Titane Grade1 Ti reste Fe0-0.2 C0-0.08 O0-0.18 N0-0.03 H0-0.015 881 3.7025 R50250 4,51 1670 80-105 16 2,2 0,45 8.4 - 10 3,7 125 - 230 350 - 760 - 35
TITANE Gr. 2 Titane Titane Grade2 Ti reste Fe0-0.3 C0-0.08 O0-0.25 N0-0.03 H0-0.015 882 3.7035 R50400 4,51 1660 80-105 16 2,2 0,45 8.4 - 10 3,7 0.31-0.37 145 - 230 410 - 780 6 - 30
YAG 250RL Aciers Maraging (Nickel Cobalt) X2 NiCoMo18-9-5+Ti Fe reste Ni17-19 Co8-10 Mo4.5-5.5 Ti0.5-0.8 C0-0.03 973 1.6358 8,10 1430-1460 185-195 19,7 0,44 9,5 0,3 2 4 3 3 3 3 3 310 - 600 1000 - 2100 -